Jamie,
To help with your question it would be helpful to have images.
If the planes are not terribly rusted, it might be fine to leave them as is. The instant rusting or 'flash' rusting happens often after a chemical clean or drying in an oven.
Of course, if you want your planes to look like new, then finding a way to shine them up is another story.
Very few of my many planes have been treated to abrasive cosmetics unless the sole needs to be worked. At one time my enthusiasm for sole lapping was a bit stronger. Now it is only done to remove rust or if there are problems which can be traced to a non-flat sole.
The Neanderthal wisdom/FAQs has a lot of information from various sources you may find helpful and informative:
https://sawmillcreek.org/showthread.php?103805
Here is an old post of mine:
https://sawmillcreek.org/showthread.php?114373
jtk
Not really, they are both part of the same tool bench. At least they are in my shop.
I have these irons and breakers in my Bedrock Planes.
A 604, 605, and 607.
http://hocktools.com/products/bl.html
Attachment 412749Attachment 412750
I started with 3 planes .. about average cost of $40
i went with a 603, 606 and found this even rustier and pitted bedrock 605 than above.
i went with white vinegar to baking soda, then used stripper for the jappaning.
i went with a 2x72 on a glass back flat platen with ceramic 120/400 belts to a scotch brite belt.
so about half way there. Awaiting new jappaning to arrive and got to do small parts tonight.
Thinking I may go fully in and just replace the blades with Lee valley
You will save yourself some effort and possible troubles by getting chip breakers with the new blades.Quote:
Thinking I may go fully in and just replace the blades with Lee valley
It sounds like you are off to a good start. Pictures of your progress are always enjoyed by others. Especially pictures of your finished planes.
jtk
I ended up using old belts yesterday in the above, but this morning felt I had to many machining marks.
so did one more grinding , but 1/10 of the time with the nice belts in 120/400 and switched from fine to medium for scotch brite. Basically got all the scratches going the same way.
That will be the the end of it as grinding can be addictive and it will never be perfect.
The last was the bedford it’s pitting was really bad.. 603,606 and 605.
before new belts.
Attachment 412755Attachment 412756Attachment 412757Attachment 412758
After in comparison to my lee valley, some character marks but that’s okay. I tried to remove the least amount of material as possible.
Attachment 412759
Nothing wrong with character marks. Scratches, dings, and patina give your planes more street cred.
I always look suspiciously at woodworkers whose tools always look like the pictures in the catalog, almost like they have never been used. . . . .
So my japanning landed from Pontytool, they were out so I had to do the waiting game started tonight !
Does anyone know for a fact if it’s 4 layers. I read that ... somewhere and couldn’t find it